OOC-G86S-A Fluid Loss Additive

ABOUT US

DICO Energy is a comprehensive energy technology company specializing in oilfield cementing chemicals, crude oil pipeline drag reducers, oilfield power equipment, and oilfield technical services.

GET A FREE QUOTE

Error: Contact form not found.

CONTACT INFO

xxxxx
info@dicoenergy.com
xxxxx
Add: Al Rusail / Al Seeb / Muscat Governorate，Sultanate of Oman

Online Support
info@dicoenergy.com
Free Contact
xxxxx

GET A QUOTE

Home
Products
Cementing Chemicals
Fluid Loss Additive
OOC-G86S-A Fluid Loss Additive

OOC-G86S-A Fluid Loss Additive

OOC-G86S-A is a type of fluid loss additive that the main component was AMPS polymers, which has good universality and can be used in a group of slurry system.
The product was suitable for a wide temperature range, and its high temperature resistance up to 230℃ . The cement slurry with this product had good fluidity, stability, less free water, no retarded effect, rapid strength development and has no special need to slurry-mixing water. Used in Both Fresh Water and Salt Water/Sea Water.

Message

Description
Parameters

Applications

The recommended operating temperature was below 230℃ (BHCT).
The recommended dosage was 0.6% (BWOC) in Fresh Water & Low Temperature and 0.6%-2.0% (BWOC) in Salt Water & High Temperature.
Packing

25kg/bag, or based on customers’ request.

Physical and Chemical Properties

Item	Index
Appearance	Light yellow powder
Bulk density, g/cm3	0.6±0.20
Solubility, %	l00
Moisture content, %	≤5.0

Cement Slurry Properties

Item	Index	Test conditions
Fluid Loss, mL	≤50	80℃, 6.9MPa
Thickening Time, min	≥60	80℃, 45MPa/45min
Initial Consistency, Bc	≤25	80℃, 45MPa/45min
Compressive Strength, MPa	≥l4	80℃, Normal pressure, 24h
Free Water, mL	≤l.0	80℃, Normal pressure
Slurry composition：l00% Class G cement (high sulfur resistant), and 44.0% (BWOC) fresh water, and 0.6% (BWOC) OOC-86S-A, and 0.5% (BWOC) OOC-X60L.